Solid & Embossed polycarbonate shet
Solid & Embossed polycarbonate sheet, Solid polycarbonate vel, PC Solid lekkens, Polycarbonate lekkens, PC lekkens, Embossed sheet
Products: Solid & Embossed polycarbonate sheet
Thickness: 0.8-12mm foar solide PC sheet, 2-5mm foar Embossed PC sheet.
Breedte: Binnen 2100mm
Length: Neffens fersiken
Kleur: Different kleuren beskikber (Clear, Brown , Blau, Grien, Grey, Red, Yellow, Sulver, etc)
Brûken:
swimbad dak, Bushalte dak, Skylite, Green hûs, etc,
Features:
1) Light gewicht
2) High ynfloed sterkte
3) Fire brânfertraagjend
4) Goede Light transmission
5) Mei UV beskerming en termyske isolaasje
6) Excellent lichaamlike, meganyske, en elektryske eigenskippen
7) Inhibits kondinsstripen
8) maat ôfmjittings, dikte en kleuren Op oanfraach beskikber.
ÛNDERDIEL | BYLD |
Solid PC sheet Thickness: 0.8-12mm Max. breedte: 1220mm | |
Embossed PC sheet Thickness: 2.0-5mm Max.width: 2100mm |
Technyske data:
Optreden | Test metoade | units | Indicators |
natuerkunde | |||
Befolkingstichtens | g / cm3 | 1.20 | |
Absorption, 24hours | ISO 62 | mg | 10 |
Water absorption, sêding / 23 ℃ | ISO 62 | % | 0.35 |
haze astm | JG / T116-200X | % | 0.53 |
Optical Eigenskippen | |||
Transmittance (6mm transparent) | JG / T 116-200X | % | 88 |
Meganyske eigenskippen | |||
Tensile opbringst stress- lateraal | JG / T 116-200X | MPa | 66 |
Tensile opbringst stress-longitudinaal | JG / T 116-200X | MPa | 66 |
Nominal stress fracture- lateraal | JG / T 116-200X | % | 95 |
Nominal stress fraktuer-fertikale | JG / T 116-200X | % | 101 |
Tensile Modulus-Transverse | JG / T 116-200X | GPA | 2.4 |
Tensile Modulus-longitudinaal | JG / T 116-200X | GPA | 2.4 |
Heating rate of feroaring fan grutte-horzontal | JG / T 116-200X | % | 0.3 |
Heating rate of feroaring fan grutte-fertikale | JG / T 116-200X | -1,55 | |
Jou punt flexural sterkte, 2mm / min | ISO 178 | MPa | 90 |
Bending Modulen, 2mm / min | ISO 178 | MPa | 2300 |
Impact Performance | |||
Charpy notched ynfloed sterkte-nivo (normaal termperture) | JG / T 116-200X | KJ / m2 | 11.0 |
Charpy kervige ynfloed sterkte-fertikale (normaal termperture) | JG / T 116-200X | KJ / m2 | 11.1 |
perforation Features | |||
maksimum penetraasje | JG / T 116-200X | 1022 | |
Maksimum penetraasje FAN enerzjy | JG / T 116-200X | 18.4 | |
Hermal performance | |||
Vicat fersêftsjen temperatuer, B / 120 | JG / T 116-200X | ℃ | 150 |
Heat ferfoarming temperatuer, 1.8 MPa | JG / T 116-200X | ℃ | 141 |
termyske conductitity | ISO 8302 | W / m ℃ | 0.2 |
Koëffisjint fan termyske útwreiding, 23-80 ℃ | ISO 11359-2 | 1 / ℃ | 7.00E-05 |
Flammability | |||
Oxygen Index | ISO 4589 | % | 25 |
flame Level | GB86240-1997 | B1 |