Khoom & embossed polycarbonate shet
Khoom & embossed polycarbonate ntawv, Khoom polycarbonate ntawv, PC Khoom los xij, polycarbonate los xij, PC los xij, embossed ntawv
cov khoom: Khoom & embossed polycarbonate ntawv
Thickness: 0.8-12mm rau khoom PC ntawv, 2-5mm rau embossed PC ntawv.
Dav: Tsis pub dhau 2100mm
Length: Raws li kev thov
xim: Ntau xim muaj (Clear, Brown , Xia, Ntsuab, Grey, liab, Daj, Silver, thiab lwm yam)
pab:
pas ua luam dej ru tsev, lub tsheb loj nres ru tsev, Skylite, Ntsuab lub tsev, thiab lwm yam,
nta:
1) Lub teeb yuag
2) High tej yam zog
3) Hluav Taws retardant
4) Zoo Lub teeb kis tau tus mob
5) Nrog UV tiv thaiv thiab thermal rwb thaiv tsev
6) rau yav tom ntej lub cev, mechanical, thiab hluav taws xob khoom
7) cheeb hws
8) Mekas qhov ntev, thickness thiab xim muaj raws li qhov kev thov.
KHOOM | daim duab |
Khoom PC ntawv Thickness: 0.8-12mm Max. dav: 1220mm | |
Embossed PC ntawv Thickness: 2.0-5mm Max.width: 2100mm |
Kev cov ntaub ntawv:
Performance | Test txoj kev | Chav | indicators |
physics | |||
ceev | g / cm3 | 1.20 | |
Haum, 24hours | ISO 62 | mg | 10 |
Dej haum, saturation / 23 ℃ | ISO 62 | % | 0.35 |
taws kub nnyiab ya ASTM | JG / T116-200X | % | 0,53 |
kho qhov muag khoom | |||
Transmittance (6mm tshab) | JG / T 116-200X | % | 88 |
NEEG KHO TSHUAB Properties | |||
Tensile tawm los stress- sab | JG / T 116-200X | MPa | 66 |
Tensile tawm los kev nyuaj siab-Longitudinal | JG / T 116-200X | MPa | 66 |
Nominal kev nyuaj siab fracture- sab | JG / T 116-200X | % | 95 |
Nominal kev nyuaj siab puas-Vertical | JG / T 116-200X | % | 101 |
Tensile modulus-transverse | JG / T 116-200X | GPA | 2.4 |
Tensile modulus-Longitudinal | JG / T 116-200X | GPA | 2.4 |
Cua sov npaum li cas ntawm kev hloov ntawm size-horzontal | JG / T 116-200X | % | 0.3 |
Cua sov npaum li cas ntawm kev hloov ntawm size-Vertical | JG / T 116-200X | -1,55 | |
Yield point FLEXURAL zog, 2 hli / min | ISO 178 | MPa | 90 |
Dabtsi yog khoov modulus, 2 hli / min | ISO 178 | MPa | 2300 |
Impact Performance | |||
Charpy Notched tej yam muaj zog-theem (qub termperture) | JG / T 116-200X | KJ / m2 | 11,0 |
Charpy Notched tej yam muaj zog-ntsug (qub termperture) | JG / T 116-200X | KJ / m2 | 11,1 |
perforation nta | |||
Maximum allergic | JG / T 116-200X | 1022 | |
Maximum allergic NTAWM zog | JG / T 116-200X | 18,4 | |
Hermal kev kawm | |||
Vicat softening kub, B / 120 | JG / T 116-200X | ℃ | 150 |
Thaum tshav kub kub distortion kub, 1.8 MPa | JG / T 116-200X | ℃ | 141 |
Thermal conductitity | ISO 8302 | W / m ℃ | 0.2 |
Coefficient ntawm thermal expansion, 23-80 ℃ | ISO 11359-2 | 1 / ℃ | 7.00E-05 |
Flammability | |||
Pa index | ISO 4589 | % | 25 |
Nplaim Theem | GB86240-1997 | B1 |