Solid & embossed polycarbonate shet
Solid & embossed polycarbonate mpempe akwụkwọ, Solid polycarbonate mpempe akwụkwọ, PC Solid Ibé akwụkwọ, polycarbonate Ibé akwụkwọ, PC Ibé akwụkwọ, Embossed mpempe akwụkwọ
Ngwaahịa: Solid & embossed polycarbonate mpempe akwụkwọ
ọkpụrụkpụ: 0.8-12mm maka siri ike PC mpempe akwụkwọ, 2-5mm maka embossed PC mpempe akwụkwọ.
Obosara: N'ime 2100mm
Ogologo: Dị ka arịrịọ
agba: iche iche na agba dị (Clear, Brown , Blue, Green, Gray, Red, Yellow, Silver, etc)
ojiji:
igwu mmiri n'elu ụlọ, Bus kwụsị n'elu ụlọ, Skylite, Green ufọk, etc,
Akụkụ:
1) Ìhè ibu
2) High mmetụta ike
3) Fire retardant
4) Good Light nnyefe
5) UV nchebe na thermal mkpuchi
6) Ezigbo anụ ahụ, n'ibu, na ọkụ Njirimara
7) na-egbochi odide
8) ngwaahia akụkụ, ọkpụrụkpụ na na agba dị n'elu arịrịọ.
Nkebi | WERE |
Solid PC mpempe akwụkwọ ọkpụrụkpụ: 0.8-12mm Max. obosara: 1220mm | |
Embossed PC mpempe akwụkwọ ọkpụrụkpụ: 2.0-5mm Max.width: 2100mm |
Nka na ụzụ data:
Performance | Test Method | Units | Indicators |
physics | |||
njupụta | g / cm3 | 1.20 | |
Absorption, 24hours | ISO 62 | mg | 10 |
Water absorption, saturation / 23 ℃ | ISO 62 | % | 0,35 |
haze ASTM | JG / T116-200X | % | 0,53 |
Optical Properties | |||
Transmittance (6mm uzo) | JG / T 116-200X | % | 88 |
n'ibu Properties | |||
Tensile mkpụrụ-esiri mpụta | JG / T 116-200X | MPa | 66 |
Tensile mkpụrụ nchegbu-longitudinal | JG / T 116-200X | MPa | 66 |
Elu ọnụ nchegbu fracture- mpụta | JG / T 116-200X | % | 95 |
Elu ọnụ nchegbu mgbaji ọkpụkpụ-Vetikal | JG / T 116-200X | % | 101 |
Tensile modulus-transverse | JG / T 116-200X | GPa | 2.4 |
Tensile modulus-longitudinal | JG / T 116-200X | GPa | 2.4 |
Heating ọnụego nke mgbanwe nke size-horzontal | JG / T 116-200X | % | 0.3 |
Heating ọnụego nke mgbanwe nke size-Vetikal | JG / T 116-200X | -1,55 | |
Mkpụrụ ebe flexural ike, 2mm / min | ISO 178 | MPa | 90 |
Ekwe Modulus, 2mm / min | ISO 178 | MPa | 2300 |
mmetụta Performance | |||
Charpy notched mmetụta ike-larịị (nkịtị termperture) | JG / T 116-200X | King James Version / m2 | 11,0 |
Charpy notched mmetụta ike-vetikal (nkịtị termperture) | JG / T 116-200X | King James Version / m2 | 11,1 |
Perforation Atụmatụ | |||
Oke penetration | JG / T 116-200X | 1022 | |
Oke penetration OF ume | JG / T 116-200X | 18,4 | |
Hermal arụmọrụ | |||
Vicat softening okpomọkụ, B / 120 | JG / T 116-200X | ℃ | 150 |
Okpomọkụ distortion okpomọkụ, 1.8 MPa | JG / T 116-200X | ℃ | 141 |
kwes conductitity | ISO 8302 | W / m ℃ | 0.2 |
Ọnụọgụ nke thermal mgbasa, 23-80 ℃ | ISO 11359-2 | 1 / ℃ | 7.00E-05 |
Flammability | |||
oxygen Index | ISO 4589 | % | 25 |
ire ọkụ Ọkwa | GB86240-1997 | B1 |