shet Polycarbonate Solid & embossed
Çarşefeke Solid & embossed Polycarbonate, sheet Polycarbonate Solid, PC Nûneratiyên Solid, Nûneratiyên Polycarbonate, Nûneratiyên PC, embossed sheet
Products: sheet Polycarbonate Solid & embossed
storis: 0.8-12mm bo sheet PC solid, 2-5mm bo sheet PC embossed.
Firehî: Di nava 2100mm
Length: Li gorî daxwazên
Color: rengên cuda License de (Clear, Brown , Blue, Hêşîn, gewr, sor, zer, Silver, hwd.)
Bikaranîna:
Hewendaway banê pool, Bus dev ji banê, Skylite, mala Green, hwd,
CÎHAN:
1) weight Light
2) hêza bandora High
3) retardant Fire
4) baş transmission Light
5) Bi parastina UV û însulasyona termal
6) fîzîkî, mekanîk, û elektrîkê milkên Nayab
7) Inhibits condensation
8) Customized aliyên bihevxistina wan û rengên License de, li ser daxwaziya.
ŞANÎ | SÛRET |
Solid sheet PC storis: 0.8-12mm Max. width: 1220mm | |
Embossed sheet PC storis: 2.0-5mm Max.width: 2100mm |
agahiyên teknîkî:
Birêvebirinî | Method Test | yekîneyên | Di dîrokê de |
fîzîkê | |||
Tîrî | g / cm3 | 1.20 | |
Absorption, 24hours | ISO 62 | mg | 10 |
avê nakêşe, saturation / 23 ℃ | ISO 62 | % | 0.35 |
ASTM Haze | JG / T116-200X | % | 0.53 |
Properties optîk | |||
Transmittance (6mm transparent) | JG / T 116-200X | % | 88 |
Properties MECHANICAL | |||
deqekê zeliqînê lateral stress- | JG / T 116-200X | mpa | 66 |
stress-Longitudinal rabûne, zeliqînê | JG / T 116-200X | mpa | 66 |
stress Nominal fracture- lateral | JG / T 116-200X | % | 95 |
stress Nominal şikestî-Dikey | JG / T 116-200X | % | 101 |
Zeliqînê Modulus-Transverse | JG / T 116-200X | GPa | 2.4 |
Zeliqînê Modulus-Longitudinal | JG / T 116-200X | GPa | 2.4 |
rêjeya germkirinê ji guhertina size-horzontal | JG / T 116-200X | % | 0.3 |
rêjeya germkirinê ji guhertina size-Dikey | JG / T 116-200X | -1,55 | |
xala Yield Mukawemeta, 2mm / min | ISO 178 | mpa | 90 |
Bending Modulus, 2mm / min | ISO 178 | mpa | 2300 |
Performance Impact | |||
Charpy bandora şeh-level hêz (termperture normal) | JG / T 116-200X | KJ / m2 | 11.0 |
Charpy şeh, bandora hêza-vertical (termperture normal) | JG / T 116-200X | KJ / m2 | 11.1 |
Features Perforation | |||
Maximum êzgeha | JG / T 116-200X | 1022 | |
Maximum êzgeha OF enerjiyê | JG / T 116-200X | 18,4 | |
performance Hermal | |||
Vicat agirê softening, B / 120 | JG / T 116-200X | ℃ | 150 |
Heat agirê berovajîkirina, 1.8 mpa | JG / T 116-200X | ℃ | 141 |
conductitity Termal | ISO 8302 | W / m ℃ | 0.2 |
Coefficient yên berfirehkirina termalê, 23-80 ℃ | ISO 11359-2 | 1 / ℃ | 7.00E-05 |
Flammability | |||
Index Oxygen | ISO 4589 | % | 25 |
Level Flame | GB86240-1997 | B1 |