Heta polycarbonate Mārō & embossed
Whārangi Mārō & embossed polycarbonate, pepa polycarbonate Mārō, PC pepa Mārō, whārangi Polycarbonate, whārangi PC, whakairo whārangi
Products: Mārō & embossed whārangi polycarbonate
Matotoru: 0.8-12mm hoki whārangi PC totoka, 2-5mm hoki whārangi PC paipera.
Whānuitanga: I roto 2100mm
Length: E ai ki tono
tae: tae rerekē e wātea ana (Ūkui, Brown , Blue, Green, Kerei, Whero, Yellow, hiriwa, etc)
Raihana:
Swimming poka tuanui, Bus mutu tuanui, Skylite, whare Green, etc,
Āhuatanga:
1) taimaha Light
2) High pānga kaha
3) Fire retardant
4) pai tuku Light
5) Ki te tiaki UV me mātao waiariki
6) pai tinana, mīhini, me hiko āhuatanga
7) inhibits tōhau
8) whakaritea āhuatanga, matotoru me ngā tae e wātea ana i runga i te tono.
ITEM | Tuhinga |
Mārō whārangi PC Matotoru: 0.8-12mm Max. whānui: 1220mm | |
Whakairo whārangi PC Matotoru: 2.0-5mm Max.width: 2100mm |
raraunga Hangarau:
mahinga | Tikanga Test | Units | tohu |
ahupūngao | |||
kiato | g / cm3 | 1.20 | |
Absorption, 24hours | ISO 62 | mg | 10 |
Water absorption, waiwai / 23 ℃ | ISO 62 | % | 0.35 |
astm Haze | JG / T116-200X | % | 0,53 |
Āhuatanga Optical | |||
Transmittance (6mm mārama) | JG / T 116-200X | % | 88 |
Āhuatanga aunoa | |||
tukua kurut lateral stress- | JG / T 116-200X | MPa | 66 |
Kurut tukua ahotea-Paetawhiti | JG / T 116-200X | MPa | 66 |
fracture- lateral ahotea iti | JG / T 116-200X | % | 95 |
ahotea iti whati-Poutū | JG / T 116-200X | % | 101 |
Kurut uara tawhiti-Tāpae | JG / T 116-200X | GPA | 2.4 |
Kurut uara tawhiti-Paetawhiti | JG / T 116-200X | GPA | 2.4 |
auau whakawera o te huringa o te rahi-horzontal | JG / T 116-200X | % | 0.3 |
auau whakawera o te huringa o te rahi-Poutū | JG / T 116-200X | -1,55 | |
wāhi Tukua flexural kaha, 2mm / min | ISO 178 | MPa | 90 |
Piko Modulus, 2mm / min | ISO 178 | MPa | 2300 |
mahinga pānga | |||
Charpy kāniwha pānga taumata kaha-(termperture noa) | JG / T 116-200X | KJ / m2 | 11.0 |
kāniwha Charpy pānga kaha-poutū (termperture noa) | JG / T 116-200X | KJ / m2 | 11.1 |
Āhuatanga Perforation | |||
ngotonga mōrahi | JG / T 116-200X | 1022 | |
penetration mōrahi o te pūngao | JG / T 116-200X | 18.4 | |
Hermal mahi | |||
Vicat tamarûraa pāmahana, B / 120 | JG / T 116-200X | ℃ | 150 |
Heat distortion pāmahana, 1.8 MPa | JG / T 116-200X | ℃ | 141 |
conductitity Thermal | ISO 8302 | W / m ℃ | 0.2 |
Tau whakarea o waiariki roha, 23-80 ℃ | ISO 11359-2 | 1 / ℃ | 7.00E-05 |
Flammability | |||
Taupū hāora | ISO 4589 | % | 25 |
Auahi Taumata | GB86240-1997 | B1 |